Customization: | Available |
---|---|
Certification: | ISO |
Surface: | Smooth |
Still deciding? Get samples of US$ 20/Piece
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment methods: |
![]() ![]() ![]() ![]() ![]() ![]() ![]() |
---|---|
Support payment in USD |
Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Test | Unit | Standard | Test Frequency |
RH75 | RH10 | RH15 | RH20 | RH30 | |
Mechanical Properties | Thickness | mm | D5199 | per roll | 0.75 | 1.00 | 1.50 | 2.00 | 3.00 |
Density | g/cc | D1505/D792 | 90,000 kg | 0.94 | |||||
Tensile Properties | D 6693 | ||||||||
· yield strength | kN/m | Type IV | 9,000 kg | 11 | 15 | 22 | 29 | 44 | |
· break strength | kN/m | 20 | 27 | 40 | 53 | 80 | |||
· yield elongation | % | 12 | 12 | 12 | 12 | 12 | |||
· break elongation | % | 700 | 700 | 700 | 700 | 700 | |||
Tear Resistance | N | D 1004 | 20,000 kg | 93 | 125 | 187 | 249 | 374 | |
Puncture Resistance | N | D 4833 | 20,000 kg | 240 | 320 | 480 | 640 | 960 | |
Stress Crack Resistance | hr. | D 5397 | per GRI GM-10 | 500 hr. | |||||
Carbon Black Content | % | D 4218 | 9,000 kg | 2.0-3.0% | |||||
Reference Propertied | Oxidative Induction Time | min | D 3895 | 90,000 kg | 100 min. | ||||
(a) Standard OIT | D 5885 | ||||||||
(b) High Pressure OIT | 400 min. | ||||||||
Oven Aging at 85°C retained after 90 days |
% | D 5721 | per each | ||||||
(a) Standard OIT - % | D 3895 | formulation | 55% | ||||||
(b) High Pressure OIT - % | D 5885 | 80% | |||||||
UV Resistance | % | per each | |||||||
High Pressure OIT - % retained after 1600 hrs |
D 5885 | formulation | 50% | ||||||
Roll Size | Roll Width | m | 7/8 | 7/8 | 7/8 | 7/8 | 7 | ||
Roll Length | m | 280 | 210 | 140 | 105 | 70 | |||
Size stability | % | 2% |